Next PPS PPSG40-02NC
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dLYymf_Next-PPS-PPSG40-02NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Polyphenylene Sulfide Glass Fiber Reinforced Natural Compound Product Applications This is High performance material & This grade is used for Appliance, Automotive, Electric/Electronics, & industrial Application Benefits Excellent Electric properties, Low warpage, good dimensional stability , High thermal stability & flame resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.65 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | |
| Across Flow | 0.25 | % | |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 100 | ||
| R-Scale | 115 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8600 | MPa | ASTM D638 |
| Tensile Strength | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus | 7800 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 275 | °C | |
| 1.8 MPa, Unannealed | 260 | °C | |
| Melting Temperature | 280 | °C | ASTM D2117 |
| RTI Elec | 240 | °C | UL 746 |
| RTI Imp | 220 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 28 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 130 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 290 to 300 | °C | |
| Middle Temperature | 310 to 320 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Mold Temperature | 130 to 145 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon G2743-01 | RheTech, Inc. | Nylon 66 | Rhelon |
| Silplus® 30 AS | Momentive Performance Materials Inc. | Silicone Rubber, HTV | Silplus® |
| TARFLON™ RY1900 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Kepital® F40-03 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| SABIC® PC PC1000R resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |