LUVOCOM® TPE-0900 VP Datasheet,TPE,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®TPE-0900 VP is a thermoplastic elastomer (TPE) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of TPE-0900 VP are: Conductivity Electrostatic protection anti-warping Wear-resistant Typical application areas include: engineering/industrial accessories Automotive Industry Handle

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Features	Conductivity Low warpage Electrostatic discharge protection Good wear resistance
Uses	Handle Engineering accessories Roller Application in Automobile Field Bearing
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	1.26	g/cm³	ISO 1183
Molding Shrinkage	0.40 - 0.80	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.50	%

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	55		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1500	MPa	ISO 527-2
Tensile Stress (Break)	38.0	MPa	ISO 527-2
Tensile Strain (Yield)	8.0	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	No Break		ISO 179/1fU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	80.0	°C	UL 746B
Maximum operating temperature- Short Term	110	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	180	°C	ISO 306/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+7	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying temperature- Hot air dryer, A	105	°C
Drying time- Hot air dryer, A	3.0 - 4.0	hr
Suggested Max Moisture	0.010	%
Rear Temperature	200 - 220	°C
Middle Temperature	210 - 230	°C
Front Temperature	210 - 230	°C
Nozzle Temperature	190 - 220	°C
Processing (Melt) Temp	210	°C
Mold Temperature	20.0 - 45.0	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.01%, otherwise molecular degradation may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture level should not exceed 0.01%, otherwise molecular degradation may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	dL9E1f_LUVOCOM-TPE-0900-VP.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
TABOREX TA 1104 HD	SILON s.ro	HDPE	TABOREX
Bynel® 41E865	DuPont Packaging & Industrial Polymers	LLDPE	Bynel®
Fainplast PVC PMS 60	Fainplast Compounds S.r.l	PVC, Flexible	Fainplast PVC
EPAMOULD 650D55	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPAMOULD
PPR PS01	Premier Plastic Resins, Inc.	PS (GPPS)	PPR