Reny® W38S2
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dKol0z_Reny-W38S2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® W38S2 is a Polyarylamide (PARA) material filled with 30% mineral. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® W38S2 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.64 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 49 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 31.2 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.44 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.12 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16200 | 15900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 121 | 111 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.90 | 0.80 | % | ISO 527-2 |
| Flexural Modulus | 15200 | 15100 | MPa | ISO 178 |
| Flexural Stress | 226 | 216 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.8 | 2.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 18 | 22 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 239 | 239 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | 206 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 2.0E+14 | -- | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 26 | -- | kV/mm | IEC 60243-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 275 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 285 | °C | |
| Nozzle Temperature | 285 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanjing Hongrui PA6 B500 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| Evolue™ SP2320 | Prime Polymer Co., Ltd. | LLDPE | Evolue™ |
| Delrin® 100T NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| HOPELEX PCG-2205 | Lotte Chemical Corporation | PC | HOPELEX |
| Karina NATURAL PVC COMPOUND 731D25/1-WK-EC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |