Purell PE 3020 K
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Purell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dK9qXa_Purell-PE-3020-K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Purell PE 3020 K is a non-additivated, low density polyethylene with high rigidity, good opticals and good chemical resistance. It is delivered in pellet form. Without exception, all potential activities for applications in the pharmaceutical, medical device, laboratory and diagnostics area have to be discussed with the relevant Technical and Business contacts first. To discuss a medical/pharmaceutical application please contact: your local Distributor or your local LyondellBasell contact. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.928 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 13.0 | MPa | ISO 527-2 |
| Coefficient of Friction (Blown Film) | > 0.80 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Recommended / Available | 15 to 40 µm | ||
| Tensile Strength | ISO 527-3 | ||
| MD : 50 µm, Blown Film | 20.0 | MPa | |
| TD : 50 µm, Blown Film | 17.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 350 | % | |
| TD : Break, 50 µm, Blown Film | 600 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 90 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 114 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20°, 50.0 µm, Blown Film | > 80 | ||
| 60°, 50.0 µm, Blown Film | > 115 | ||
| Haze (50.0 µm, Blown Film) | < 7.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy 1(50.0 µm) | 55.0 | J/cm | DIN 53373 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 287 TFE 10 | RTP Company | Nylon 66 | RTP |
| NEXUS PS 625 | Nexus Resin Group, LLC. | PS (HIPS) | NEXUS PS |
| ASI POLYPROPYLENE 1329 | A. Schulman Inc. | PP Copolymer | ASI POLYPROPYLENE |
| LNP™ LUBRICOMP™ DFL38 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |
| Rotuba CAB B9024 (10% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |