Clearflex® H&T DFH 20
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dHW0a2_ClearflexHampTDFH20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex DFH 20 is a Linear Low Density Polyethylene Resin butene comonomer produced by Unipol gas phase technology. Clearflex DFH 20 exhibits a typical wide molecular weights distribution which gives an excellent processability together with good mechanical characteristics. Main Applications Clearflex DFH 20 is mainly designed for the production of micro-irrigation tubes, durable hoses and pipes, extruded profiles and for the production by injection molding of fittings. The outdoor use, requires the additivation with anti-UV, to maintain excellent performance even after prolonged periods of exposure to sunlight. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | > 500 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 44 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, molding | 11.0 | MPa | ISO 527-2 |
| Fracture, molding | 15.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | > 800 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 310 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elmendorf Tear Strength 1 | |||
| MD : 25.0 µm | 10.0 | kN/m | |
| TD : 25.0 µm | 255.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 110 | °C | ISO 306/A |
| Melting Temperature | 120 | °C | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® FX30C | BASF Leuna GmbH | Nylon 6 | Miramid® |
| Smooth-Cast® 305 | Smooth-On, Inc | PUR, Unspecified | Smooth-Cast® |
| Amilan® CM3006G-30 | Toray Resin Company | Nylon 66 | Amilan® |
| GLS PP ZT89 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| KPOL-PP K-PPC 20.0 | KPOL Chem Co. | PP Impact Copolymer | KPOL-PP |