Moplen HP527J
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dGvgYh_Moplen-HP527J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP527J is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP), especially for high shrinkage memory film. It contains a standard processing stabilisation but does not contain any slip, antiblocking agents and it is Calcium Stearate free. Moplen HP527J typical applications are BOPP shrinkage tobacco films in blends with hydrogenated hydrocarbon resins. For regulatory information please refer to Moplen HP527J Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | 70 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1450 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 34.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 11 | % | ISO 527-2/50 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus - 1% Secant, MD 1(20 µm) | 2700 | MPa | Internal method |
| Tensile Strength - MD 2(Break, 20 µm) | 135 | MPa | Internal method |
| Tensile Elongation - MD 3(Break, 20 µm) | 32 | % | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 85.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 156 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 0.70 | % | ASTM D1003 |
| Additional Information |
|---|
| Typical Film Properties of monolayer film produced on a laboratory simultaneous film stretcher (7x7@150°C) |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E General Purpose GM-3255 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E General Purpose |
| RheTech Thermoplastic Polyolefin FT4900-74UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| RJM SN504 | RJM International, Inc. | Nylon 6 | RJM |
| Sinvicomp SFC8210 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Active Flow LP1040T | SCG Chemicals Co., Ltd. | PE Homopolymer | Active Flow |