SOLLAMID A 2700 - A 2730 FV 15
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Krisoll Resinas Plásticas Ltda. |
| Trademark: | SOLLAMID |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dElS1M_SOLLAMID-A-2700---A-2730-FV-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SOLLAMID A 2700 - A 2730 FV 15 is a Polyamide 66 (Nylon 66) material filled with 15% glass fiber. It is available in Latin America. Primary attribute of SOLLAMID A 2700 - A 2730 FV 15: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.23 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.70 | -- | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.1 | -- | % | ASTM D570 |
| Heat Stability | 100 to 110 | -- | °C |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 122 | 107 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 4300 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 120 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | 7.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 5200 | 3300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 160 | 110 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Unnotched Izod Impact Strength (23°C) | 8.0 | 13 | kJ/m² | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | > 200 | -- | °C | |
| 1.8 MPa, Unannealed | > 240 | -- | °C | |
| Melting Temperature | 250 to 260 | -- | °C | |
| CLTE - Flow | 3.0E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | ASTM D257 |
| Dielectric Strength | 21 | -- | kV/mm | ASTM D149 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax SE012 | LyondellBasell Industries | PP Impact Copolymer | Pro-fax |
| Baoding 67I85 | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU-Polyester | Baoding |
| Andur AL 95 AP | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Vipel® F701-S-SPT-23 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Durethan® BKV 215 H2.0 901510 | LANXESS GmbH | Nylon Copolymer | Durethan® |