ASTALAC™ ABS M190
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dE1TXk_ASTALAC-ABS-M190.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ASTALAC™ ABS M190 is a general purpose ABS injection moulding grade and offers an optimum balance of impact toughness, product rigidity, heat resistance and mouldability. Typical applications include vacuum cleaner casings, electronic consumer goods assemblies, whitegoods fascia panels and handles, coffin fittings and handles as well as telecommunications equipment. Note: The letters "UV" or "W" indicate UV stabilisation has been added [ ie: ASTALAC™ ABS M190UV ]. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 19 | g/10 min | |
| 230°C/3.8 kg | 5.0 | g/10 min | |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.20 mm) | 41.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 55 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2250 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 71.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 280 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.20 mm | 77.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 83.0 | °C | |
| 1.8 MPa, Unannealed, 12.7 mm | 88.0 | °C | |
| Vicat Softening Temperature | 102 | °C | ASTM D1525 5 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (1.60 mm) | 550 | °C | AS/NZS 60695 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 205 to 225 | °C | |
| Middle Temperature | 215 to 235 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 60.0 to 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 3.0 to 6.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 700 GB 20 Z | RTP Company | HDPE | RTP |
| RTP 102 GB 25 | RTP Company | PP Homopolymer | RTP |
| Trademark PE LLB1918B | Trademark Plastics Corporation | LLDPE | Trademark PE |
| TOTAL Polypropylene PPH 4022 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| LNP™ COLORCOMP™ 144C compound | SABIC Innovative Plastics | PC | LNP™ COLORCOMP™ |