LNP™ STAT-LOY™ 63000CT compound
| Category: | PC+Polyester , Polycarbonate + Polyester |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dDg2rW_LNP-STAT-LOY-63000CT-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A permanent antistatic PC-Alloy compound that features transparency and superior cleanliness for advanced semiconductor packaging applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.70 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1160 | MPa | ASTM D638 |
| -- | 1180 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 35.0 | MPa | ASTM D638 |
| Yield | 34.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 200 | % | Internal Method |
| Break | 140 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 1160 | MPa | ASTM D790 |
| -- 5 | 1140 | MPa | ISO 178 |
| Flexural Strength 6(Break, 50.0 mm Span) | 50.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 69 | kJ/m² | ISO 179/2C |
| Notched Izod Impact (23°C) | 580 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 83.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 6.40 mm | 73.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 7 | 68.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+11 to 5.0E+12 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+11 to 5.0E+12 | ohms·cm | ASTM D257 |
| Static Decay 8 | 2.0 | sec | FTMS 101B |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2540 µm) | 81.0 | % | ASTM D1003 |
| Haze (2540 µm) | 10 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 95.0 | °C | |
| Drying Time | 6.0 to 8.0 | hr | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 225 to 240 | °C | |
| Front Temperature | 230 to 250 | °C | |
| Nozzle Temperature | 230 to 250 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 10 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 mm |
| 8 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer E81H | Precision Polymer Engineering Ltd. | EPDM | Precision Polymer |
| Sylvin 2936-90 White 1505 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| WINDFORM® PS | CRP Technology s.r.l. | PS (Specialty) | WINDFORM® |
| ACCUCOMP™ ABS802L | ACLO Compounders Inc. | ABS | ACCUCOMP™ |
| MAJORIS GFR307 - 8229 | AD majoris | PP, Unspecified | MAJORIS |