GLS PP YT49
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | GLS Polymers Pvt. Ltd. |
| Trademark: | GLS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dDSrEU_GLS-PP-YT49.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PP 20 TALC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 to 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 to 10 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 23.0 to 27.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 5.0 | % | ASTM D638 |
| Flexural Modulus | 1800 to 2000 | MPa | ASTM D790 |
| Flexural Strength | 25.0 to 30.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 55 to 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 75.0 to 80.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 32.0 to 64.0 | °C | |
| Injection Pressure | 65.0 to 105 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SORVEX 1200 | Sorensen Ventures | PBT | SORVEX |
| Nypol® PA A3 G33 HS NTLA013 NR307 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| HI-ZEX™ 3600F | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Leona™ 93G33 | Asahi Kasei Chemicals Corporation | Nylon 66 | Leona™ |
| POFEX EP8300S 85A/85C | POLYROCKS CHEMICAL CO., LTD | TPU, Unspecified | POFEX |