EVAL™ E105
| Category: | EVOH , Ethylene Vinyl Alcohol |
| Manufacturer: | Kuraray Co., Ltd. |
| Trademark: | EVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dC8uFF_EVAL-E105.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
44 mol% Ethylene Vinyl Alcohol Copolymer E105A - non-lubricated pellets E105B - Pellets are lubricated to facilitate material feeding into extruder |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 5.7 | g/10 min | |
| 210°C/2.16 kg | 13 | g/10 min | |
| Ethylene Content | 44.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 80 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 11 | % | ISO 527-2 |
| Flexural Modulus | 4800 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Permeability | ISO 14663-2 | ||
| 20°C, 0% RH | 0.016 | cm³·mm/m²/atm/24 hr | |
| 20°C, 65% RH | 0.030 | cm³·mm/m²/atm/24 hr | |
| 20°C, 85% RH | 0.066 | cm³·mm/m²/atm/24 hr | |
| Water Vapor Transmission Rate 1(40°C, 90% RH) | 0.83 | g·mm/m²/atm/24 hr | ASTM E96 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 2.0 | kJ/m² | ISO 179/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 53.0 | °C | ISO 11357-2 |
| Melting Temperature | 165 | °C | ISO 11357 |
| Peak Crystallization Temperature | 145 | °C | ISO 11357-3 |
| Note Message | |
|---|---|
| 1 . | Procedure E |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 3084H | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Converge® Polyol 212-20 | Novomer, Inc. | PC | Converge® |
| Karina BLACK PVC COMPOUND -E 75900-48/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PETILEN S 39/71 | PETKIM Petrokimya Holding A.S. | PVC, Flexible | PETILEN |
| Wanthane® WHT-8190RV | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | Wanthane® |