Moplen HP520H
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dBl8T4_Moplen-HP520H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen HP520H is a polypropylene homopolymer especially designed for the production of biaxially oriented polypropylene films (BOPP). It contains a general purpose formulation. Typical applications of Moplen HP520H are film for adhesive tapes and general packaging. For regulatory information please refer to Moplen HP520H Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 71 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 34.0 | MPa | ISO 527-2/50 |
| Break | 23.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 12 | % | |
| Break | > 500 | % | |
| Flexural Modulus (23°C) | 1450 | MPa | ISO 178 |
| Coefficient of Friction 1(Dynamic) | 0.50 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Tangent (20 µm) | 2900 | MPa | Internal Method |
| Tensile Strength - MD 2(Break, 20 µm) | 250 | MPa | ASTM D882 |
| Tensile Elongation - MD 3(Break, 20 µm) | 90 | % | ASTM D882 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 93.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 155 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 4(45°) | 91 | Internal Method | |
| Haze 5(20.0 µm) | 0.40 | % | Internal Method |
| Note Message | |
|---|---|
| 1 . | MTM17029E |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | MA 17021 |
| 5 . | MA 17031 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Premier HD10H50 | Premier Polymers, LLC. | HDPE | Premier |
| Yanshan PE LD615 | SINOPEC Beijing Yanshan Petrochemical | LDPE | Yanshan PE |
| Fainplast PVC CKL 79 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Huafon JF-PDY-511H | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LOXIM 510 01HB | LOXIM Industries Private Limited | PC+ABS | LOXIM |