Order Products : sales@su-jiao.com
ISPLEN® PM276EV
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dB7VhU_ISPLENPM276EV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ISPLEN® PM276EV is a copolymer 16% mineral fillers reinforced. It shows a high impact resistance with an excellent scratch resistance, and good stiffness and demoulding properties during the transformation process. The product is UV stabilised. APPLICATIONS
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.990 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.77 | % | ISO 294-4 |
| Flow | 0.75 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2100 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 17.0 | MPa | ISO 527-2 |
| Fracture | 20.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 16 | % | ISO 527-2 |
| Fracture | 4.0 | % | ISO 527-2 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 2.3 | kJ/m² | ISO 179 |
| -20°C | 2.7 | kJ/m² | ISO 179 |
| 23°C | 9.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 45 | kJ/m² | ISO 179 |
| -20°C | 53 | kJ/m² | ISO 179 |
| 0°C | 83 | kJ/m² | ISO 179 |
| 23°C | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 73.0 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 53.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ISO 306/A120 |
| -- | 66.0 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 190 - 250 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP562 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| TAISOX 3314 | Formosa Plastics Corporation | LLDPE | TAISOX |
| Zhongfa PA6 BZR8 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Nylon 6 | Zhongfa |
| Baoding 6185B | Baoding Bangtai Polymeric New-Materials Co.,Ltd | TPU, Unspecified | Baoding |
| Hanwha Total PP KB71 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |