VITAMIDE® TS10BK8517
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dAPFzV_VITAMIDE-TS10BK8517.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® TS10BK8517 is a Polyamide 66/6 Copolymer (Nylon 66/6) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 85.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 120 | MPa | ISO 178 |
| Break | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 190 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 240 | °C | ASTM D2117, ISO 1218 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 26 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Malen E FGNX 23-D006 | LyondellBasell Industries | LDPE | Malen |
| Daplen™ EE158AIB | Borealis AG | TPO | Daplen™ |
| Hostaform® S 9363 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Lionpol HF-203021 | Lion Polymers Incorporated | TPE | Lionpol |
| LNP™ THERMOCOMP™ RF00ASXZ compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |