SABIC® LDPE 2004CX3
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dAIDRI_SABIC-LDPE-2004CX3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2004CX3 is an Ultra Melt Strength (UMS) grade typically used in foam applications. Application SABIC® LDPE 2004CX3 can be typically used for all types of foam, produced with chemical blowing agents or physical gases, X-linked and non X-linked. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.6 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 44 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 240 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 86.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 107 | °C | DIN 53765 |
| Peak Crystallization Temperature (DSC) | 96.0 | °C | DIN 53765 |
| Heat of Fusion | 107 | J/g | DIN 53765 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultrason® E 2010 G4 MR SW 15102 | BASF Corporation | PESU | Ultrason® E |
| Nypol® PA B3 HL UV PRTA011 NT340 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| AKROMID® A3 GF 55 black (2654) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| Hylex® P1010G40HB | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| XENOY™ 5220U resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |