TOTAL Polyethylene Lumicene® M 1820 EP
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polyethylene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d9hVW3_TOTAL-Polyethylene-Lumicene-M-1820-EP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lumicene® mPE M 1820 EP is a Metallocene based Low Density Polyethylene with hexene as comonomer. Lumicene® mPE M 1820 EP is especially dedicated to film applications where outstanding mechanical and optical properties are required. Moreover it offers excellent sealing behavior at low temperature. Lumicene® mPE M 1820 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first general metallocene based polyethylene. Furthermore, Lumicene® mPe M 1820 EP has a very low gel level. Lumicene® mPE M1820 EP is suited for many applications such as:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 10.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 10.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 59.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 55.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 640 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 710 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | > 1000 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40.0 µm | 114.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 162.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 103 | °C | ISO 306 |
| Melting Temperature | 110 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 72 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 5.2 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 | °C |
| Extrusion instructions |
|---|
| BUR: 1.5:1 to 4.5:1Die Gap: 0.8 to 2.8 mmLaboratory test specimens produced with the following extrusion conditions: 45 mm screw diameter, L/D = 30, die diameter = 120 mm, die gap = 1.4 mm, BUR = 2.5:1, temperature = 210°C. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 399 X 121668 B | RTP Company | PC | RTP |
| RTP 307 SE | RTP Company | PC | RTP |
| NEO-ZEX™ 0134M | Prime Polymer Co., Ltd. | LLDPE | NEO-ZEX™ |
| APEX® 84842-C | Teknor Apex Company | PVC, Flexible | APEX® |
| Latene® 7H2W T-V0E | LATI S.p.A. | PP Homopolymer | Latene® |