Reny® 4001
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d8xcdk_Reny-4001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Reny® 4001 is a Polyarylamide (PARA) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Reny® 4001 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 5.0 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 3.40 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.38 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.090 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 17900 | 14700 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 124 | 126 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.90 | 1.1 | % | ISO 527-2 |
| Flexural Modulus | 16600 | 14100 | MPa | ISO 178 |
| Flexural Stress | 204 | 188 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.2 | 4.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 19 | 17 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 236 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 224 | 213 | °C | ISO 75-2/A |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 265 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Yuyao PET PETG20 | Yuyao Tenglong Plastics Co., Ltd. | PET | Yuyao PET |
| Clariant Nylon 6 PA-213XO12 | Clariant Corporation | Nylon 6 | Clariant Nylon 6 |
| Huafon JF-P-6270 / JF-I-4118 | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| LNP™ THERMOCOMP™ DF008ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| MAXAMID™ PA6G50HSL-NC010 | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |