Geon™ Vinyl Dry Blend E7009
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Dry Blend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d8CQ3V_Geon-Vinyl-Dry-Blend-E7009.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bendable, low elastic memory effect |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 1-22434-42-0000 | ASTM D4216 | |
| PVC Cell Classification | 12364 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3070 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 47.0 | MPa | ASTM D638 |
| Flexural Modulus | 3320 | MPa | ASTM D790 |
| Flexural Strength | 84.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 64 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 74.7 | J/cm | ASTM D4226 |
| 23°C 4 | 141 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 5 | 79.4 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 6 | 78.3 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 7 | 78.3 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 8 | 73.9 | °C | ASTM D648 |
| CLTE - Flow | 5.9E-5 | cm/cm/°C | ASTM D696 |
| Additional Information |
|---|
| Physical properties based on Geon E7009 white 1024 lot# UTCX 57572 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| 5 . | Annealed at 60 deg.C |
| 6 . | Annealed at 50 deg.C |
| 7 . | Annealed at 60 deg.C |
| 8 . | Annealed at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD A 380 | RTP Company | PC | RTP |
| Shin-Etsu Elastomer KE-2090-10A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| WELLAMID Nylon 6000 GVS 10/30 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| Hylon® N1020HL | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| EnviroTPO 2512 | West Michigan Compounding | Polyolefin, Unspecified | EnviroTPO |