EMERGE™ PC 4350 Advanced Resin is a polycarbonate resin offering ultraviolet light stability, high heat resistance and maximum toughness. This UV stable resin is available in a full range of colors that can be customer tailored to meet your product requirements. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2410 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 60.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 71.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 6.0 | % | |
| Break, 3.20 mm, Injection Molded | 150 | % | |
| Flexural Modulus (3.20 mm, Injection Molded) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 850 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm, Injection Molded) | No Break | ASTM D256 | |
| Instrumented Dart Impact (23°C, 3.20 mm, Injection Molded, Total Energy) | 87.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed | 143 | °C | |
| 1.8 MPa, Unannealed | 127 | °C | |
| 1.8 MPa, Annealed | 140 | °C | |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 1 |
| Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 271 to 288 | °C | |
| Mold Temperature | 65.6 to 98.9 | °C |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Microthene® G MN71020 | LyondellBasell Industries | LDPE | Microthene® G |
| ALTECH® PA6 C 3230/100 GB20 GF10 | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| ExxonMobil™ LLDPE LL 3001.63 | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| Karina GRAY PVC COMPOUND 600D18/136-A-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina CLEAR PVC COMPOUND -E 75/232-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |