LNP™ THERMOCOMP™ UX05504 compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d827uy_LNPTHERMOCOMPUX05504compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP UX05504 is a compound based on Polyphthalamide resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound UF-1007 HS S Product reorder name: UX05504 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 12.6 | MPa | ISO 527-2 |
| Fracture | 164 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 10000 | MPa | ISO 178 |
| Flexural Stress | 295 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1(23°C) | 7.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 39 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed, 64.0 mm Span) | 260 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Aegis® CSDE Generation II | Honeywell | Nylon, Unspecified | Aegis® |
| Bayfit® SA512 (85 Index) | Covestro - PUR | PUR, Unspecified | Bayfit® |
| Borealis PE BB2581 | Borealis AG | HDPE | Borealis PE |
| Andur 8003 AS/Ethacure® 100LC | Anderson Development Company | PUR-TDI | Andur |
| GELOY™ XP4045LG resin | SABIC Innovative Plastics | ASA+PC | GELOY™ |