BCC Resins BC 6008
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BCC Products Inc. |
| Trademark: | BCC Resins |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d6SKrT_BCC-Resins-BC-6008.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BCC Resins BC 6008 is an Epoxy; Epoxide (Epoxy) product. It can be processed by spraying and is available in North America. Typical application: Coating Applications. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 85 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 42.1 | MPa | ASTM D638 |
| Flexural Strength (Break) | 60.0 | MPa | ASTM D790 |
| Compressive Strength | 85.5 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 58.3 | °C | ASTM D648 |
| CLTE - Flow | 4.1E-5 | cm/cm/°C | ASTM D696 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 31 Mix Ratio by Weight: 25 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 100 | ||
| Pot Life (24°C) | 15 to 18 | min | |
| Demold Time (24°C) | 480 to 720 | min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-4001 | Teknor Apex Company | TPE | Telcar® |
| APEX® 588 | Teknor Apex Company | PVC, Flexible | APEX® |
| Geon™ HTX E1502 | PolyOne Corporation | PVC Alloy | Geon™ HTX |
| HIDEN® P301E BL | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| Karina MBPP BLUE 600/167-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |