Order Products : sales@su-jiao.com
VITAMIDE® AB36NT8514
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d5ybZg_VITAMIDE-AB36NT8514.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® AB36NT8514 is a Polyamide 66 (Nylon 66) product filled with 30% glass bead. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 2.0 | g/10 min | ISO 1133 |
| Water Absorption (23°C, 24 hr) | 1.0 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 9.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3900 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 130 | MPa | ISO 178 |
| Break | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 35 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 225 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 95.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 30 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 450 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 | |
| Oxygen Index | 25 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ DC-818.G001-8000 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| Clariant ABS ABS3460 | Clariant Corporation | ABS | Clariant ABS |
| KOPA® KN133G30BLL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Plaslube® J-1/30/TF/13/SI/2 NAT | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| Latigray 82-02 CX/80 | LATI S.p.A. | Nylon 12 | Latigray |