Borstar® HE6067

Category:	HDPE , High Density Polyethylene
Manufacturer:	Borealis AG
Trademark:	Borstar®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cyly6l_Borstar-HE6067.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Borstar HE6067 is a black high density (HD) jacketing compound, which is produced with the Borealis proprietary Borstar bimodal process technology.

Borstar technology allows the manufacturing of polymers outside the traditional MFR and density range making it possible to optimize processability, reduce shrinkage and yet with excellent physical toughness and environmental stress crack resistance (ESCR) properties.

Borstar HE6067 contains 2.5% well-dispersed carbon black in order to ensure excellent weathering resistance.

Borstar HE6067 offers substantially reduced shrinkage which helps to maintain low signal attenuation for fibre optic communication cables and low jacket retraction for energy cables in combination with excellent mechanical and barrier properties. Borstar HE6067 offers a balance of properties giving advantages in manufacturing, installation and lifetime performance of communication and energy cables.

Borstar HE6067 meets the applicable requirements as below when processes using sound extrusion practice and testing procedure:

ASTM D 1248 Type III, Class C, Category 3, Grade J4, E8, E9, W8

BS 6234: Type H2C, TS2

DIN 57818/VDE 0818

DIN VDE 0207, Type 2YM3

HD 620 S1, Part 1, table 4B, DMP 2, 8-12, 14, 15

IEC 60502, Type ST7

IEC 60708

IEC 60840, ST7

ISO 1872-PE, KCHL, 40 D-022

General Information
Additive	Carbon black (3%)
Features	Moisture resistance High ESCR (Stress Cracking Resistance) Good UV resistance Workability, good Good wear resistance Scratch resistance Good weather resistance Heat resistance, high Good toughness Low shrinkage High hardness
Uses	Communication Cable Jacketing Cable sheath Wire and cable applications
Agency Ratings	DIN VDE 0207 Type 2YM3 HD 620 S1 Part 1, table 4B, DMP 2, 8-12, 14, 15 IEC 60502 Type ST7 IEC 60708 IEC 60840 Type ST7
Appearance	Black
Forms	Particles
Processing Method	Extrusion

Physical	Nominal Value	Unit	Test Method
Density			ISO 1183
-- ¹	0.954	g/cm³	ISO 1183
Matrix resin ²	0.942	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.7	g/10 min	ISO 1133
Environmental Stress-Cracking Resistance ³(50°C, 10% Igepal, F0)	> 5000	hr	IEC 60811-4-1/B

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness
Shaw D, 1 sec	61		ISO 868
Shaw D, 3 seconds	58		DIN 53505

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	29.0	MPa	ISO 527-2/50
Tensile Strain (Break)	900	%	ISO 527-2/50
Flexural Modulus	900	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Brittleness Temperature	< -76.0	°C	ASTM D746

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity ⁴	1.0E+16	ohms·cm	IEC 60093
Dielectric Strength	20	kV/mm	IEC 60243-1

Additional Information	Nominal Value	Unit	Test Method
Pressure Test ⁵(115°C)		%	IEC 60811-3-1

Extrusion	Nominal Value	Unit
Drying Temperature	< 90.0	°C
Melt Temperature	180 - 190	°C

Extrusion instructions
Preheating: < 90 °CCooling water: 60 °C

Note Message
1 .	Compound
2 .	ISO 1872-2
3 .	No crack
4 .	Compound
5 .	at high temperature, 6 hrs

Resin Grade	Manufacturer	Category	Trademark
Staramide P1000J5	Eurostar Engineering Plastics	Nylon 6	Staramide
Novamid® 2020J	DSM Engineering Plastics	Nylon 66/6	Novamid®
AKROMID® B3 GF 30 S1 natural (1383)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
APEX® 3708-73NT	Teknor Apex Company	PVC, Flexible	APEX®
Paryls® PPSU F1350	Youju New Materials Co., Ltd.	PPSU	Paryls®