LNP鈩?THERMOCOMP鈩?OF008G compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cxRt1Q_LNP-THERMOCOMP-OF008G-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP OF008G is a compound based on PPS - Linear containing 15% Glass Fiber, 25% Milled Glass. Also known as: LNP* THERMOCOMP* Compound OF-1008 MG Product reorder name: OF008G |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.20 to 0.50 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8850 | MPa | ASTM D638 |
| Tensile Strength 2(Break) | 104 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 1.9 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 9310 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 157 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 400 | J/m | ASTM D4812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218 V40 BLACK 21 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Spartech Polycom PP5133R B1 | Spartech Polycom | PP Homopolymer | Spartech |
| MULTICHEM™ 6014 | Colorite Polymers | PVC, Unspecified | MULTICHEM™ |
| Karina COMP. PVC CRYSTAL -E 70/264 | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |
| LNP™ LUBRICOMP™ SP003 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |