LNP™ COLORCOMP™ PX99848 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ COLORCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cxLvKr_LNP-COLORCOMP-PX99848-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP COLORCOMP PX99848 is an unfilled Nylon 6 resin. Also known as: LNP* COLORCOMP* Compound PDX-P-99848 Product reorder name: PX99848 |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.2 | % | |
| Across Flow : 24 hr | 1.4 | % | |
| Water Absorption (24 hr, 50% RH) | 1.3 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3470 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 76.5 | MPa | |
| Break | 76.5 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 3.5 | % | |
| Break | 4.5 | % | |
| Flexural Modulus | 2890 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 640 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 180 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 57.2 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 266 to 277 | °C | |
| Front Temperature | 277 to 288 | °C | |
| Processing (Melt) Temp | 266 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinko-Lac® ABS 1002 | Mitsubishi Rayon America Inc. | ABS | Shinko-Lac® |
| COSMOTHENE® F410-6 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® |
| Delrin® 300CP NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| INNOPOL® PP CS 3-9120 SR5 | Inno-Comp Ltd. | PP, Unspecified | INNOPOL® PP |
| Sylvin 8707-80 White 1576 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |