HiFill® PA6/6,6 IM3 BK
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | HiFill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cx3Ayz_HiFill-PA6-6-6-IM3-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HiFill® PA6/6,6 IM3 BK is a Polyamide 66/6 Copolymer (Nylon 66/6) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.8 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 50 | % | ASTM D638 |
| Flexural Modulus | 2650 | MPa | ASTM D790 |
| Flexural Strength | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 130 | J/m | |
| 23°C, 3.18 mm | 640 | J/m | |
| Unnotched Izod Impact (3.18 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 204 | °C | |
| 1.8 MPa, Unannealed | 60.0 | °C | |
| CLTE - Flow | 7.9E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 2.0 to 4.0 | % | |
| Rear Temperature | 266 to 304 | °C | |
| Middle Temperature | 266 to 304 | °C | |
| Front Temperature | 266 to 304 | °C | |
| Processing (Melt) Temp | 260 to 282 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell RP315M | LyondellBasell Industries | PP Random Copolymer | Purell |
| Beamset 750 | Arakawa Chemical Industries, Ltd. | Acrylic, Unspecified | Beamset |
| Elastane™ 4720-80A | Technical Polymers, LLC | TPU-Polyester | Elastane™ |
| Haysite SMC 46000 | Haysite Reinforced Plastics | Polyester, TS | Haysite SMC |
| Sylvin 8200-90 White 1569 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |