| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | DAIKIN AMERICA, INC. |
| Trademark: | DAI-EL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cuxES4_DAI-EL-G-717.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| DAI-EL G-717 is a cure-incorporated copolymer designed for transfer and compression molding applications. G-717 offers moderate cure speeds with good elongation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.81 | g/cm³ | ASTM D792 |
| Mooney Viscosity (ML 1+10, 121°C) | 37 | MU | ASTM D1646 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 69 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (100% Strain) | 3.00 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 13.7 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 270 | % | ASTM D412 |
| Additional Information |
|---|
| All tests performed were performed under DAIKIN test methodsFluorine Content: 66%Curing characteristic, Measuring Temperature: 170°CCuring characteristic, Curelastomer: 3.8 min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ HDPE DGDC-2100 NT 7 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| Hiprolon® 400 VN | Arkema | Nylon 1012 | Hiprolon® |
| Hostacom EBG733T | LyondellBasell Industries | PP Copolymer | Hostacom |
| LNP™ LUBRICOMP™ Noryl_SPN422L compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |
| PLEXIGLAS® Sheet Mutlicolored | Evonik Industries AG | Acrylic (PMMA) | PLEXIGLAS® Sheet |