LNP™ STAT-LOY™ LAT4000 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | csXlNo_LNP-STAT-LOY-LAT4000-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* STAT-LOY* LAT400 is an antistatic compound based on Polycarbonate containing proprietary fillers. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 65.7 | MPa | Internal Method |
| Tensile Elongation (Break) | 220 | % | Internal Method |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 86.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 830 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 130 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | ASTM D257 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.20 | ||
| 60 Hz | 3.20 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 206 B | RTP Company | Nylon 610 | RTP |
| RTP 4000 MG 50 SI 2 | RTP Company | PPA | RTP |
| Sinpolene MBN4032 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| Topolymer® 5711-801M | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Sylvin 7833-70C Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |