PALSAFE® R 15
| Category: | PC , Polycarbonate |
| Manufacturer: | pal plast GmbH |
| Trademark: | PALSAFE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | crTA55_PALSAFE-R-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PALSAFE®R 15 is a polycarbonate (PC) product,. It can be processed by injection molding and is available in Europe. PALSAFE®R 15 applications include electrical/electronic applications and electrical appliances. Features include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 14.5 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield, 23°C) | 61.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield, 23°C) | 5.0 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break (23°C) | 50 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 144 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 275 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-2 | UL 94 |
| Additional Information |
|---|
| Melt-Volume Flow Rate, ISO 1133, 300°C/1.2 kg: 12 to 17 cm³/10 minTensile Modulus, ISO 527, 23°C, 1 mm/min, Type A: 2200 to 2400 MPaTensile Stress at Yield, ISO 527, 23°C, 50 mm/min, Type A: 59 to 63 MPaTensile Strain at Yield, ISO 527, 23°C, 50 mm/min, Type A: 4 to 6 %Nominal Tensile Strain at Break, ISO 527, 23°C, 50 mm/min, Type A: >50 %Vicat Softening Temperature, ISO 306, B50 (50°C/h 50N): 142 to 145 °CDensity, ISO 1183: 1.18 to 1.2 g/cm³Water Absorption, ISO 62, 23°C, Saturation: 0.2 to 0.4 %Moisture Absorption, ISO 62, 23°C, 50% RH: 0.15 to 0.2 % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNO ALPHALOY MPC2501LG | Techno Polymer Co, Ltd. | PC+ABS | TECHNO ALPHALOY |
| Ultramid® B3WG10 BK00564 | BASF Corporation | Nylon 6 | Ultramid® |
| AKROMID® B3 GK 30 black (1827) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Ferro PP LPP40BK80HB NATURAL | Ferro Corporation | PP, Unspecified | Ferro PP |
| ALTECH® PC ECO 1000/141 FR IM | ALBIS PLASTIC GmbH | PC | ALTECH® PC |