SLOVASTER® B1 GF 30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Plastcom |
| Trademark: | SLOVASTER® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cplDKE_SLOVASTER-B1-GF-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT for injection moulding, chemically reinforced with 30% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending, tensial strength, toughness. Does not absorb water, that means that identical properties are maintained also in wet environment. Melt is characterised by very good rheology, which enables manufacturing of extremely multiple products with complicated downflow-path. Anisotropy of shrinkage is much better in comparison with PA, what influences the manufacturing of round, cylindric or other hole products. Application in the automotive, electrical and engineering industry - connectors of cable harnesses, car-door locks, connection links, grips etc. Delivered in natural mode and in the full RAL colour scale. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.55 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | STM 64 0808 | ||
| Across Flow | 1.2 | % | |
| Flow | 0.82 | % | |
| Water Content | 0.050 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 6700 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -20°C | 8.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -20°C | 55 | kJ/m² | |
| 23°C | 55 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 205 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 200 | °C | ISO 306/B |
| Melting Temperature (DSC) | 200 to 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Electric Strength | 33 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Ignition Temperature | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 100 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC87-30I | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| 3M™ Dyneon™ Fluoroplastic FEP 6303Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| APEX® 3600-70NT | Teknor Apex Company | PVC, Flexible | APEX® |
| Latamid 66 E21 G/15 | LATI S.p.A. | Nylon 66 | Latamid |
| KYDEX® XD03 | SEKISUI Polymer Innovations, LLC | PMMA+PVC | KYDEX® |