Injection moulding grade, mineral-reinforced, heat stabilised for under the bonnet covers, fuel lids

General Information
Filler / Reinforcement	Mineral, 30% Filler by Weight
Additive	Heat Stabilizer
Features	Crystalline Fuel Resistant Good Dimensional Stability Good Flow Good Stiffness Good Surface Finish Grease Resistant Heat Stabilized Oil Resistant Solvent Resistant
Uses	Automotive Applications Caps Closures Engineering Parts Housings
Appearance	Black
Forms	Pellets
Processing Method	Injection Molding
Resin ID (ISO 1043)	(PA66+PA6)-M30

Physical	Dry	Conditioned	Unit	Test Method
Density
--	1.38	--	g/cm³	ISO 1183
--	1380	--	kg/m³	ISO 1183 ¹
Water Absorption
Saturation, 23°C	6.5 to 7.5	--	%	ISO 62
Saturation	7.0	--	%	ISO 62 ²
Equilibrium, 23°C, 50% RH	2.2	--	%	ISO 62
Equilibrium	2.2	--	%	ISO 62 ³
Viscosity Number
96% H2SO4 (Sulphuric Acid)	140	--	cm³/g	ISO 307
--	140	--	cm³/g	ISO 307, 1157, 1628 ⁴

Hardness	Dry	Conditioned	Unit	Test Method
Ball Indentation Hardness	180	--	MPa	ISO 2039-1

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
23°C	5200	1900	MPa	ISO 527-2
--	5200	1900	MPa	ISO 527-2 ⁵
Tensile Stress
Break, 23°C	8.00	40.0	MPa	ISO 527-2
Break	80.0	40.0	MPa	ISO 527-2 ⁶
Tensile Strain
Break, 23°C	3.0	30	%	ISO 527-2
Break	3.0	30	%	ISO 527-2 ⁷
Flexural Modulus (23°C)	4800	1300	MPa	ISO 178
Flexural Stress				ISO 178
--	--	35.0	MPa
23°C	130	--	MPa

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength
-30°C	3.0	--	kJ/m²	ISO 179/1eA
23°C	3.5	5.0	kJ/m²	ISO 179/1eA
-30°C	3.00	--	kJ/m²	ISO 179/1eA ⁸
23°C	3.50	5.00	kJ/m²	ISO 179/1eA ⁹
Charpy Unnotched Impact Strength
-30°C	50	--	kJ/m²	ISO 179/1eU
23°C	60 kJ/m²	No Break		ISO 179/1eU
-30°C	50.0	--	kJ/m²	ISO 179/1eU ¹⁰
23°C	60.0 kJ/m²	No Break		ISO 179/1eU ¹¹

Thermal	Dry	Conditioned	Unit	Test Method
Melting Temperature	260	--	°C	ISO 11357-3, ISO 3146

Flammability	Dry	Conditioned	Unit	Test Method
Burning Rate (1.00 mm)	< 100	--	mm/min	FMVSS 302
Flame Rating (1.50 mm)	HB	--		UL 94
Burning Behav. at thickness h (1.50 mm)	HB	--		ISO 1210 ¹²
Glow Wire Flammability Index (1.00 mm)	650	--	°C	IEC 60695-2-12

Additional Information	Dry	Conditioned		Test Method
Automotive Materials (> 1.00 mm)	+	--		FMVSS 302

Injection	Dry	Unit
Processing (Melt) Temp	280 to 300	°C
Mold Temperature	80.0 to 100	°C

Extrusion	Dry	Unit
Melt Temperature	280 to 300	°C

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
11 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
NaturePlast PBE 006	NaturePlast	Polyester, TP	NaturePlast
Dryflex® A2 602709	ELASTO	SEBS	Dryflex®
Globalene® ST869K	Lee Chang Yung Chemical Industry Corp.	PP Random Copolymer	Globalene®
EPAMOULD 655D55	Epaflex Polyurethanes S.R.L.	TPU-Polyester	EPAMOULD
StarClear® 1040-0000	Star Thermoplastic Alloys & Rubbers, Inc.	TPE	StarClear®