Tenac™ FS410
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | Tenac™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cpA9XQ_Tenac-FS410.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tenac™ FS410 is an Acetal (POM) Homopolymer product. It is available in Africa & Middle East, Asia Pacific, Europe, or North America. Applications of Tenac™ FS410 include engineering/industrial parts and housings. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.8 to 2.2 | % | Internal Method |
| Water Absorption (23°C, 24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3100 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield | 65.0 | MPa | ISO 527-2 |
| -- | 66.0 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break | 20 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2730 | MPa | ASTM D790 |
| -- | 3000 | MPa | ISO 178 |
| Flexural Strength | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Notched Izod Impact | 41 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 172 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 164 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 136 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 100 | °C | ISO 75-2/A |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP562 | Southern Polymer, Inc. | LDPE | PRIMALENE |
| Hanwha Total PP GH42F | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina GRAY PVC COMPOUND 880-18/402-F-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1301/CF/10/GF/20/GK/20/BK100 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| POLYfill PPC B10075 | Polykemi AB | PP Copolymer | POLYfill |