Vitaster® UP36NT6639
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Vitaster® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | co1Uc9_Vitaster-UP36NT6639.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vitaster® UP36NT6639 is a Polybutylene Terephthalate (PBT) product filled with 15% glass bead and 15% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.20 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5900 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 120 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 26 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 180 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 225 | °C | ISO 1218, ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Comparative Tracking Index | |||
| Solution A | 300 | V | IEC 60112 |
| -- | 300 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 21 | % | ASTM D2863, ISO 4589-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PPR-30G Nat | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Ravamid® R210 T53 | Ravago Group | Nylon 66 | Ravamid® |
| Dynalloy™ OBC8000-T05 | PolyOne Corporation | TPE | Dynalloy™ |
| Plenco 02535 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |
| LNP™ THERMOCOMP™ LF004E compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |