LubriOne™ ATH-000/04S NATURAL
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cnGlSn_LubriOne-ATH-000-04S-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 2.0 to 4.0 | % | |
| Across Flow | 1.0 to 3.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1930 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 50.3 | MPa | |
| Break | 50.3 | MPa | |
| Flexural Modulus 3 | 2270 | MPa | ASTM D790 |
| Flexural Strength 4 | 75.8 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Steel - Dynamic | 0.11 | ||
| vs. Steel - Static | 0.15 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.35 mm, Injection Molded) | 60 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 158 | °C | |
| 1.8 MPa, Unannealed | 86.7 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 | °C | |
| Drying Time | 2.0 | hr | |
| Mold Temperature | 60.0 to 71.1 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax RP913J | LyondellBasell Industries | PP Random Copolymer | Pro-fax |
| Starex SF-0505HWR | SAMSUNG SDI CO., LTD. | MABS | Starex |
| NaturePlast PEVE 010 | NaturePlast | HDPE | NaturePlast |
| Hapflex™ 566-3 | Hapco Inc. | TP, Unspecified | Hapflex™ |
| NORYL™ V0150B resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |