Order Products : sales@su-jiao.com
SABIC® HDPE F00950
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cmPw8U_SABIC-HDPE-F00950.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® HDPE F00950 resin is a high molecular weight, high density polyethylene copolymer. The design of the product, molecular architecture and density, gives F00950 a good balance of easy extrusion and high melt strength with strong physical properties. SABIC® HDPE F00950 is typically used for production of thin films with good strength and rigidity. The material contains anti-oxidants. Typical applications SABIC® HDPE F00950 resin is typically used for blown film extrusion and production of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products. Processing conditions SABIC® HDPE F00950 can be extruded on conventional HMW-HDPE equipment with temperature settings between 200 and 220°C. Film properties Film properties have been measured at 25 µm films with a BUR = 4. Film has been produced on Kiefel IBC film blown line at 160 kg/h with a die of 150 mm, die gap of 1.2 mm and a frostline height of 150 cm (= 10D). This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.070 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 8.5 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.30 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 25 µm, blown film | 620 | MPa | ISO 527-3 |
| TD : 25 µm, blown film | 620 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 25 µm, blown film | 30.0 | MPa | ISO 527-3 |
| TD : Yield, 25 µm, blown film | 30.0 | MPa | ISO 527-3 |
| MD : Broken, 25 µm, blown film | 40.0 | MPa | ISO 527-3 |
| TD : Broken, 25 µm, blown film | 50.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 25 µm, blown film | > 300 | % | ISO 527-3 |
| TD : Broken, 25 µm, blown film | > 400 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength (25.0 µm) | 350 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 6383-2 | ||
| MD : 25.0 µm | 6.0 | kN/m | ISO 6383-2 |
| TD : 25.0 µm | 20.0 | kN/m | ISO 6383-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEMICOSIL® 936 UV | Wacker Chemie AG | Silicone | SEMICOSIL® |
| VAMPSON L 3010 | Vamp Tech | PPS | VAMPSON |
| Niuk YPC4008 | Shanghai Niuk New Plastic Technology Co., Ltd. | Acetal (POM) Copolymer | Niuk |
| LUVOCOM® PEEK CLASSIX 7918 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Hostacom M2 R18 NAT | LyondellBasell Industries | PP Homopolymer | Hostacom |