TAROLOX 111 G9
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLOX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cllTYG_TAROLOX-111-G9.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PET glass fiber reinforced 45%, very high temperature resistance, very good chemical resistance, very good mechanical, thermal and electrical properties, very low moisture absorption, very good dimensional stability. Product must be dryed before moulding. Available: all colors, heat stabilized (H), release agent (W). |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 to 1.70 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.15 to 0.25 | % | |
| Across Flow | 0.40 to 0.60 | % | |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570, ISO 62 |
| Granule Humidity | < 0.030 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 15500 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 185 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 13500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 280 | MPa | ISO 178 |
| Break | 280 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 11 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | 60 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact | ISO 180, ASTM D256 | ||
| -20°C, 3.20 mm | 90 | J/m | |
| 23°C, 3.20 mm | 120 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 248 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 3 | 140 | °C | IEC 60216 |
| -- | 140 | °C | UL 746B |
| Vicat Softening Temperature | 245 | °C | ISO 306/B50, ASTM D1525 4 |
| Melting Temperature | 256 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 2.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.00 mm) | 32 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | ||
| 1.60 mm | HB | ||
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 22 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 90.0 to 130 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | 200000 hrs |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X3687 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Spartech Polycom SCR1-5010 | Spartech Polycom | ABS | Spartech |
| Flontech® FT-EK20-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Karina IVORY PVC COMPOUND -E 700-35/1-EX | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ESTOPLAST XU 240NN01 | Ester Industries Ltd. | Nylon 6 | ESTOPLAST XU |