CELEX™ 3600-20
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CELEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ckOsx1_CELEX-3600-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CELEX 3600-20 contains non-chlorinated, non-brominated & phosphate flame retardant and suitable for use by injection molding applications in the computer, electronics, electrical, and information technology equipment markets. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2300 | MPa | ASTM D638 |
| Tensile Strength (Yield, 3.20 mm, Injection Molded) | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 110 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2400 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 93.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 680 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded) | 127 | °C | ASTM D648 |
| CLTE - Flow | 1.2E-4 | cm/cm/°C | ASTM D696 |
| RTI Elec | 125 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 1 | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.50 mm | 5VA | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN JHC-374 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| Vi-Chem PVC VDM93 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Unichem 6811-02 BUSCH | Colorite Polymers | PVC, Unspecified | Unichem |
| FORMULA P ELAN XP 422 | Putsch Kunststoffe GmbH | PP+Styrenic | FORMULA P |
| LNP™ THERMOCOMP™ UF00AAS compound | SABIC Innovative Plastics Europe | PPA | LNP™ THERMOCOMP™ |