LNP™ THERMOCOMP™ RX06420 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ckBzSG_LNP-THERMOCOMP-RX06420-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RX06420 is a compound based on Nylon 66 resin containing 20% Glass Fiber. Added features of this material include: Easy Molding, Low Extractable, Mold Release. Also known as: LNP* THERMOCOMP* Compound RF-1004 EM LE MR Product reorder name: RX06420 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 1.0 to 3.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | |||
| 50.0 mm Span 1 | 5990 | MPa | ASTM D790 |
| -- 2 | 5580 | MPa | ISO 178 |
| Flexural Strength 3(Break, 50.0 mm Span) | 161 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 44 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 400 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 219 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.3 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALFILL H 07 S 40 MJ | RIALTI Srl | PP Homopolymer | RIALFILL |
| ColorRx® TPE-B95A0RXCL | LTL Color Compounders, Inc. | TPE | ColorRx® |
| Geon™ Vinyl Flexible XV3901 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hypro® PPH-T10 | Entec Polymers | PP Homopolymer | Hypro® |
| Sylvin 9659-55 Blue 8360 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |