Ebalta LH 22 / GL
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | chzw1q_Ebalta-LH-22-GL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ebalta LH 22 is an epoxy laminating resin, which, depending on its application, can be used with the slow GL hardener or the faster GR hardener. They distinguish by minimal physiolgical effects. Regarding dimensional accuracy and -stability, laminates made of ebalta LH 22, even come up to great demands. Due to its long potlife ebalta LH 22/GL is especially suitable for large-area and thick laminates, which also with a thickness of more than 10 mm, applied in one step, cure without any shrinkage at room temperature. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Shore Hardness (Shore D) | 83 to 89 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 3810 to 4110 | MPa | ISO 178 |
| Flexural Stress | 90.0 to 110 | MPa | ISO 178 |
| Compressive Stress | 94.2 to 95.8 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 15 to 22 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 62.0 to 66.0 | °C | ISO 75-2/B |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 25 | ||
| Resin | Mix Ratio by Weight: 100 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.32 to 1.38 | g/cm³ | |
| Viscosity (25°C) | 1.1 to 1.5 | Pa·s | |
| Curing Time (20°C) | 16 to 24 | hr | |
| Pot Life 1(20°C) | 40 to 45 | min |
| Note Message | |
|---|---|
| 1 . | 200 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIME TPO E-2900H | Prime Polymer Co., Ltd. | PP Homopolymer | PRIME TPO |
| Nymax™ GF1200 A15 NC011 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Asrene® UF 1820S1 | Chandra Asri Petrochemical | LLDPE | Asrene® |
| Exxelor™ PE 1040 | ExxonMobil Chemical | TP, Unspecified | Exxelor™ |
| LEXAN™ LUX9132C resin | SABIC Innovative Plastics | PC | LEXAN™ |