FRAGOM PR/420 NAT P
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | FRAGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | chxQUk_FRAGOM-PR-420-NAT-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
FRAGOM PR PR/420 NAT P is a flame retardant halogen free polyolefin thermoplastic commpounds. FRAGOM PR PR/420 NAT P is a flame retardant polyolefin thermoplastic compound having high temperature index and good oxygen index, suitable for cable sheathing and insulation. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.53 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 160°C/21.6 kg | 6.0 to 15 | g/10 min | |
| 190°C/21.6 kg | 2.0 to 7.0 | g/10 min | |
| Water Absorption - 9 hr (70°C) | < 1.0 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hot Pressure Test - Penetration (90°C) 1 | 30 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conductivity | < 4.00 | µS/mm | IEC 60754-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Corrosive Gas in Smoke - pH | > 4.50 | IEC 60754-2 | |
| Halogen Content | 0 | % | IEC 60754-1 |
| Smoke Density | ASTM E662 | ||
| Flaming Mode, Ds max 2 | 54 | ||
| Non-flaming Mode, Ds max 3 | 200 | ||
| Temperature Index (Burning) 4 | 330 | °C | NES 715 |
| Toxicity | < 1.5 | % | CEI 20-37 Part 2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 53 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 13.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 180 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (110°C, 168 hr) | 13 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (110°C, 168 hr) | -22 | % | IEC 60811 |
| Change in Tensile Stress | |||
| in Hydrocarbons | -10 | % | ENI 018 100 |
| 70°C, 4 hr, in SAE 20 Oil | 12 | % | IEC 60811 |
| Change in Tensile Strain at Break | |||
| in Hydrocarbons | -15 | % | ENI 018 100 |
| 70°C, 4 hr, in SAE 20 Oil | -16 | % | IEC 60811 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | > 43 | % | ASTM D2863 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 to 70.0 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Cylinder Zone 1 Temp. | 100 | °C | |
| Cylinder Zone 2 Temp. | 110 | °C | |
| Cylinder Zone 3 Temp. | 145 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Cylinder Zone 5 Temp. | 175 | °C | |
| Die Temperature | 180 | °C |
| Note Message | |
|---|---|
| 1 . | K=0.6, 6 hr |
| 2 . | 8 min |
| 3 . | 13 min |
| 4 . | 21% O2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 6610/60 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| ALTECH® PA66 A 1000/109 YL2492-12LS | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Magnobond 91 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| OnFlex™ S HF 60A-3S1982 | PolyOne Corporation | TPE | OnFlex™ |
| LNP™ LUBRICOMP™ DZL24 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |