| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | KMI Group, Inc. |
| Trademark: | KMI PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cg9kFA_KMIPEKM3416CDMD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KM-3416CDMD is a high density polyethylene for blow molding Applications: Large Articles |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | 1100 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 65 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 34.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 890 | % | ASTM D638 |
| Flexural Modulus | 1030 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength | 357 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 67.0 | °C | ASTM D648 |
| Brittleness Temperature | -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Melting Temperature | 131 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 125 | °C | Internal method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stylac™ T8701 | Asahi Kasei Chemicals Corporation | AS | Stylac™ |
| AEI SX490:CM401 and SX490:CM401-2 | AEI Compounds Limited | LDPE | AEI |
| Durethan® BKV 60 H2.0 EF DUS060 900116 | LANXESS GmbH | Nylon 6 | Durethan® |
| HAIPLEN EP10 G6 BA | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| Plenco 07487 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |