| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Osterman & Company |
| Trademark: | Osterlene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cdQdUw_Osterlene-HI-8-2-3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HI-8-2.3 is a Injection Molding grade designed to provide good processability while maintaining a fine balance of mechanical properties. With HI-8-2.3's combination of processability and high impact strength, it is suitable for a wide variety of applications such as office accessories, housewares, appliance parts and electrical/electronic housings. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 55 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2140 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 21.0 | MPa | ASTM D638 |
| Fracture | 20.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 55 | % | ASTM D638 |
| Flexural Modulus 1 | 1650 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 31.6 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Annealed) | 79.4 | °C | ASTM D648 |
| Vicat Softening Temperature | 97.2 | °C | ASTM D1525 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 45 | ASTM D523 |
| Additional Information |
|---|
| HI-8.0-2.3z has a CSA 0.6HB flame rating. |
| Note Message | |
|---|---|
| 1 . | Method I (three-point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Geon™ Vinyl Flexible 90067 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Lustran® SMA 2316 | INEOS ABS (USA) | SMA | Lustran® ABS |
| omay® V42 | Suzhou OMAY Optical Materials Co., Ltd | Film, PC | omay® |
| Polygen SG6R | Shanghai Polygen Science and Technology Co., Ltd. | PPS | Polygen |
| LNP™ THERMOCOMP™ DF0029ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |