Amodel® AT-1125 HS polyphthalamide (PPA) is a toughened, heat stabilized 25% glass reinforced resin, designed as a cost effective solution for applications requiring stiffness, good dimensional stability, chemical resistance and ductility. This resin has a high heat deflection temperature and a high flexural modulus, with greater tensile elongation than untoughened glass-reinforced PPA. Typical applications include bearings, bearing retainers/cages, housings, chemical processing equipment components, motor frames, sporting equipment, lawn and garden equipment and components that require press-fit or snap-fit assembly. Black: AT-1125 HS BK 324

General Information
Filler / Reinforcement	Glass fiber reinforced material, 25% filler by weight
Additive	Impact modifier heat stabilizer
Features	Good dimensional stability Impact modification Good chemical resistance Heat resistance, high Thermal Stability
Uses	Lawn and Garden Equipment Electrical appliances Industrial components Industrial application Machine/mechanical parts Home appliance components Metal substitution Connector Parts under the hood of a car Automotive Electronics Application in Automobile Field Fuel line General Shell Bearing
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.35	--	g/cm³	ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	0.40	--	%	ASTM D955
Transverse flow	0.60	--	%	ASTM D955
Water Absorption (24 hr)	0.20	--	%	ASTM D570

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus
--	8480	--	MPa	ASTM D638
--	8890	--	MPa	ISO 527-2
Tensile Strength
Fracture	174	--	MPa	ASTM D638
Fracture	190	--	MPa	ISO 527-2
Tensile Elongation
Fracture	3.2	--	%	ASTM D638
Fracture	2.5	--	%	ISO 527-2
Flexural Modulus
--	7580	7580	MPa	ASTM D790
--	7790	--	MPa	ISO 178
Flexural Stress
--	240	--	MPa	ISO 178
Yield	255	200	MPa	ASTM D790

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength	8.8	--	kJ/m²	ISO 179/1eA
Notched Izod Impact
--	120	85	J/m	ASTM D256
--	8.8	--	kJ/m²	ISO 180/1A
Unnotched Izod Impact	1100	800	J/m	ASTM D256
Instrumented Dart Impact				ASTM D3763
Energy as Maximum Load ¹	--	1.90	J	ASTM D3763
Total Energy	--	9.36	J	ASTM D3763
Total energy	13.8	--	J	ASTM D3763
Maximum load energy ²	2.03	--	J	ASTM D3763

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, not annealed	279	--	°C	ASTM D648
1.8 MPa, not annealed	235	--	°C	ASTM D648
1.8 MPa, not annealed	280	--	°C	ISO 75-2/A
Melting Temperature	311	--	°C	ISO 11357-3, ASTM D3418

Injection	Dry	Unit
Drying Temperature	121	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.10	%
Hopper Temperature	79.4	°C
Rear Temperature	304 - 318	°C
Front Temperature	316 - 329	°C
Processing (Melt) Temp	321 - 343	°C
Mold Temperature	135	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Note Message
1 .	Maximum Load: 230 lb (1020 N)
2 .	Maximum load: 280 lb (1240 N)

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ccMkqe_Amodel-AT-1125-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Toughblend® PA66-1600	Colour Image Plastic Compound Sdn. Bhd. (CIPC)	Nylon 6	Toughblend®
ULTEM™ foam DU319	SABIC Innovative Plastics Asia Pacific	PEI	ULTEM™ foam
ICORENE® 1901	ICO Polymers EMEA, A Division of A. Schulman	Plastomer	ICORENE®
Iupilon® GMB1110	Mitsubishi Engineering-Plastics Corp	PC+Polyester	Iupilon®
SABIC® SUPEER™ 8315	Saudi Basic Industries Corporation (SABIC)	mLLDPE	SABIC® SUPEER™