Grilamid® XE 4107 black 9992
| Category: | Nylon 6/12 , Polyamide 6/12 Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cbX9Tf_Grilamid-XE-4107-black-9992.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilamid® XE 4107 black 9992 is a Polyamide 6/12 Copolymer (Nylon 6/12) material. It is available in Asia Pacific, Europe, or North America for injection molding. Important attributes of Grilamid® XE 4107 black 9992 are:
Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.0 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 1.8 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 200 | 155 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 12500 | 9500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 175 | 135 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | 5.5 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 16 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 90 | 85 | kJ/m² | |
| 23°C | 85 | 85 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 185 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 115 | -- | °C | ISO 75-2/C |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 90.0 to 120 | -- | °C | |
| -- 2 | 180 | -- | °C | |
| Melting Temperature 3 | 215 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.0E-5 | -- | cm/cm/°C | |
| Transverse | 1.0E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+12 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 36 | 36 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA612, MHR, 18-120, GF40 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Silamid® E | Roonamid a.s. | Nylon 6 | Silamid® |
| AKROTEK® PK-VM TM natural (4954) | AKRO-PLASTIC GmbH | PK-Aliphatic | AKROTEK® |
| LUVOCOM® GS-58 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| Hifax X 4305 HL86 S01261 | LyondellBasell Industries | PP Copolymer | Hifax |
| LGS 5Z 500 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGS |