Chemlon® MDF35 Datasheet,Nylon 6,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
MDF35 is a 35% glass fibre reinforced nylon 6 that offers superior mechanical performance coupled with good surface finish.finish and mould release characteristics.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 35% filler by weight
Features	Good demoulding performance Excellent appearance
Processing Method	Injection molding

Physical	Dry	Conditioned	Unit	Test Method
Density	1.41	--	g/cm³	ISO 1183
Molding Shrinkage ¹	0.70 - 1.2	--	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.9	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	10000	8000	MPa	ISO 527-2
Tensile Stress	180	120	MPa	ISO 527-2
Tensile Strain (Break)	4.0	6.0	%	ISO 527-2
Flexural Modulus	9200	4500	MPa	ISO 178
Flexural Stress	260	140	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength	17	37	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	55	--	kJ/m²	ISO 179/1eU
Notched Izod Impact	14	--	kJ/m²	ISO 180/A

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	> 200	--	°C	ISO 75-2/B
1.8 MPa, not annealed	> 200	--	°C	ISO 75-2/A

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+15	1.0E+12	ohms	IEC 60093
Volume Resistivity	1.0E+17	1.0E+14	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	11	8.0	kV/mm	IEC 60243-1
Relative Permittivity	3.80	4.20		IEC 60250
Comparative Tracking Index	500	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating (0.750 mm, UL listing - Black only)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	80.0	°C
Drying Time	20	hr
Rear Temperature	250 - 280	°C
Middle Temperature	250 - 280	°C
Front Temperature	250 - 280	°C
Processing (Melt) Temp	250 - 290	°C
Mold Temperature	70.0 - 90.0	°C
Injection Rate	Fast
Back Pressure	Low
Screw Speed	Moderate

Injection instructions
No drying is necessary unless the material has been exposed to air for longer than three hours. The appearance of splash marks on the surface of mouldings indicates excessive moisture is present.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, moulding shape and processing conditions. The range values given are determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Chemlon®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cZtSUy_Chemlon-MDF35.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RAMOFIN PPC365T8	Polyram Ram-On Industries	PP Copolymer	RAMOFIN
SCANAMID 6 B32^E F15	Polykemi AB	Nylon 6	SCANAMID 6
Akulon® F136-E2	DSM Engineering Plastics	Nylon 6	Akulon®
Globalprene® 3537	Lee Chang Yung Chemical Industry Corp.	SBS	Globalprene®
Hifax CA 7153 S	LyondellBasell Industries	PP Random Copolymer	Hifax