Hostalen PP H5416
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostalen PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cYmpw9_Hostalen-PP-H5416.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostalen PP H5416 is a natural polypropylene random copolymer. The product has a high heat- and extremely high extraction stability. For regulatory information please refer to Hostalen PP H5416 Product Stewardship Bulletin ( PSB ). It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.897 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/5.0 kg | 0.50 | g/10 min | |
| 230°C/2.16 kg | 0.30 | g/10 min | |
| 230°C/5.0 kg | 1.3 | g/10 min | |
| Viscosity Number (Reduced Viscosity) | 420.0 | ml/g | ISO 1628 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 3 sec) | 65 | ISO 868 | |
| Ball Indentation Hardness (H 132/30) | 45.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 850 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 24.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 13 | % | ISO 527-2/50 |
| Flexural Modulus (23°C) | 850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| 0°C | 12 | kJ/m² | |
| 23°C | 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 70.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 49.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 132 | °C | ISO 306/A50 |
| -- | 69.0 | °C | ISO 306/B50 |
| Melting Temperature 1 | 141 | °C | ISO 11357-3 |
| CLTE - Flow (23 to 80°C) | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.24 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 to 280 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 200 to 230 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min, 2nd heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2600H0 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| NILAMID® A3 W GF55 | Nilit Plastics | Nylon 66 | NILAMID® |
| Abstron TIM300 | Bhansali Engineering Polymers Limited | ABS+Acrylic | Abstron |
| LNP™ LUBRICOMP™ DCL32 compound | SABIC Innovative Plastics Europe | PC | LNP™ LUBRICOMP™ |
| LNP™ THERMOCOMP™ DF004ER compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |