ACRYLITE® Hi-Gloss FT15

Category:	Acrylic (PMMA) , Polymethyl Methacrylate Acrylic
Manufacturer:	Evonik Cyro LLC
Trademark:	ACRYLITE®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cYdcxs_ACRYLITE-Hi-Gloss-FT15.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

ACRYLITE® Hi-Gloss FT15 polymer is an amorphous thermoplastic molding and extrusion compound based on polymethyl methacrylate (PMMA). ACRYLITE® Hi-Gloss FT15 polymer is available in a range of opaque colors including deep jet black.

Typical properties of ACRYLITE® Hi-Gloss acrylic polymers are:

excellent weather resistance

high light transmission

high mechanical strength

high surface hardness and mar resistance

good melt flow rate

versatile colorability due to crystal clarity

The special properties of ACRYLITE® Hi-Gloss FT15 polymer are:

high heat resistance

available in transparent and a range of opaque colors

medium melt flow rate

AMECA listed

Application:
Used for injection molding and extrusion applications.

General Information
Features	Amorphous Good Colorability Good Flow Good Weather Resistance High Clarity High Hardness High Heat Resistance High Strength Scratch Resistant
Uses	Automotive Applications Automotive Exterior Trim Lighting Fixtures
Agency Ratings	EC 1907/2006 (REACH)
Appearance	Black Colors Available Opaque
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Density	1.19	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	4.50	cm³/10min	ISO 1133

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	3500	MPa	ISO 527-2/1
Tensile Stress (Break)	50.0	MPa	ISO 527-2/5
Tensile Strain (Break)	3.1	%	ISO 527-2/5

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	18	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	107	°C	ISO 75-2/B
1.8 MPa, Unannealed	105	°C	ISO 75-2/A
Glass Transition Temperature	121	°C	IEC 1006
Vicat Softening Temperature	115	°C	ISO 306/B50

Flammability	Nominal Value	Unit	Test Method
Glow Wire Ignition Temperature	675	°C	IEC 60695-2-13
Fire Rating	B2		DIN 4102

Resin Grade	Manufacturer	Category	Trademark
PRIMALENE WPP692M	Southern Polymer, Inc.	mLLDPE	PRIMALENE
Silopren® LSR 2050	Momentive Performance Materials Inc.	Silicone Rubber, LSR	Silopren®
NORYL™ 731 resin	SABIC Innovative Plastics	PPE+PS	NORYL™
Clyrell RC249R	LyondellBasell Industries	PP Random Copolymer	Clyrell
Five Plus™ CPP30C	Noble Polymers	PP Copolymer	Five Plus™