MAJORIS AG200

Category:	PP, Unspecified , Polypropylene
Manufacturer:	AD majoris
Trademark:	MAJORIS
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cYPAsM_MAJORIS-AG200.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

AG200 is a 20% chemically coupled glass fibre reinforced polypropylene compound intended for extrusion profile and blow moulding.

The product is available in natural, but other colours can be provided on request.

AG200 has been developed especially for demanding applications in various engineering sectors.

AG200 has high rigidity and impact strength, very good long term heat resistancy, good dimensional stability and good creep resistancy also at high temperatures.

APPLICATIONS
AG200 is recommended for the extrusion of profiles (automotive parts, building, electrical, furniture and construction profiles or pipes).

General Information
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Features	Chemically Coupled Good Creep Resistance Good Dimensional Stability High Heat Resistance High Impact Resistance High Rigidity Recyclable Material
Uses	Automotive Applications Building Materials Construction Applications Electrical/Electronic Applications Furniture Piping Profiles
Appearance	Colors Available Natural Color
Forms	Pellets
Processing Method	Blow Molding Extrusion Pipe Extrusion Profile Extrusion

Physical	Nominal Value	Unit	Test Method
Density	1.04	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	0.70	g/10 min	ISO 1133
Molding Shrinkage	0.90 to 1.1	%	Internal Method

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Break)	76.0	MPa	ISO 527-2/50
Tensile Strain (Break)	5.0	%	ISO 527-2/50
Flexural Modulus ¹	4300	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	13	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	38	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	141	°C	ISO 75-2/B
1.8 MPa, Unannealed	132	°C	ISO 75-2/A

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	220	°C
Cylinder Zone 2 Temp.	220	°C
Cylinder Zone 3 Temp.	230	°C
Cylinder Zone 4 Temp.	240	°C
Melt Temperature	210 to 240	°C
Head Temperature	240	°C
Die Temperature	230	°C

Note Message
1 .	2.0 mm/min

Resin Grade	Manufacturer	Category	Trademark
RTP 705	RTP Company	HDPE	RTP
Sevrene® 3500-60A	Vi-Chem Corporation	TPE	Sevrene®
Trademark PE HDP0353	Trademark Plastics Corporation	HDPE	Trademark PE
LightSpan® LS-3441	NuSil Technology	Silicone	LightSpan®
Karina BLACK PVC COMPOUND TR-641D48/1-IS-BZ	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina