Pearlthane® 11T65D
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cXoqkC_Pearlthane-11T65D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlthane® 11T65D is a polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, combining very high hardness with excellent mechanical properties. It is especially designed for injection moulding. Pearlthane® 11T65D is very adequate for the production of shoe heels and top pieces, as well as technical parts. It is also suitable for the production of compounds for the automotive industry. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.20 | g/cm³ | ASTM D792 |
| 20°C | 1.20 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 64 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 527 | ||
| 100% strain | 25.0 | MPa | ASTM D412, ISO 527 |
| 300% strain | 31.0 | MPa | ASTM D412, ISO 527 |
| Tensile Strength (Yield) | 35.0 | MPa | ASTM D412, ISO 527 |
| Tensile Elongation (Break) | 440 | % | ASTM D412, ISO 527 |
| Tear Strength | |||
| -- 1 | 210 | kN/m | ASTM D624 |
| -- | 210 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 35 | % | ASTM D395B |
| 70°C, 22 hr | 50 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | -23.0 | °C | ISO 11357-2 |
| Melting Temperature 3 | 205 - 215 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 220 | °C | |
| Middle Temperature | 225 | °C | |
| Front Temperature | 230 | °C | |
| Nozzle Temperature | 225 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing Force: 30 tonsScrew Diameter: 30 mmMaximum Hydraulic Pressure: 210 barMold: Plaque 120x120x2 mm |
| Note Message | |
|---|---|
| 1 . | C mould |
| 2 . | 10°C /min |
| 3 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shinblend® A274G20 | Shinkong Synthetic Fiber Corp. | PC+PBT | Shinblend® |
| UNIBRITE® UB-700A | Nippon A&L Inc. | AES | UNIBRITE® |
| GAPEX® HPP30GR55NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| Hanwha Total PP TB53 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Complet® LCF5-LGF15-PP | PlastiComp, Inc. | PP Homopolymer | Complet® |