LNP™ LUBRICOMP™ AL003 compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cXmbBR_LNPLUBRICOMPAL003compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* AL003 is a compound based on Acrylonitrile Butadiene Styrene resin containing PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound AL-4030 Product reorder name: AL003 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.60 - 0.80 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.80 - 1.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.80 - 1.0 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.60 - 0.80 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.20 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.31 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2410 | MPa | ASTM D638 |
| -- | 2290 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 35.9 | MPa | ASTM D638 |
| Yield | 35.0 | MPa | ISO 527-2 |
| Fracture | 32.4 | MPa | ASTM D638 |
| Fracture | 32.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.3 | % | ASTM D638 |
| Yield | 2.7 | % | ISO 527-2 |
| Fracture | 15 | % | ASTM D638 |
| Fracture | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2060 | MPa | ASTM D790 |
| -- | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 62.1 | MPa | ASTM D790 |
| -- | 61.9 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 200 | J/m | ASTM D4812 |
| 23°C 3 | 21 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 11.4 | J | ASTM D3763 |
| -- | 8.23 | J | ISO 6603-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5014L HPT | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| PRIMALENE WPP721 | Southern Polymer, Inc. | HDPE | PRIMALENE |
| GLS Blends LY609 | GLS Polymers Pvt. Ltd. | Nylon 66+PP | GLS Blends |
| Elastron® D D101.A90.N | Elastron USA, Inc. | SBS | Elastron® D |
| HDPE NG 7000 H | The Dow Chemical Company | HDPE | HDPE |